      为了确保美国ACCU达因笔测试结果的可重复性，材料的准备和测试的方法必须标准化。ASTM STD D6182协议规定了测试条件以及方法。遗憾的是，这个协议不适用于胶片的测试。测试时间的范围在24小时到72小时，这种苛刻的要求也许对于R&D 是有适合的，但对于普通的QC 测试来说，所设定的时间也许短了一点。检测理论认为将周围环境，基材，和测试方法的标准化是很重要的，。培训师教导检测人员要将所有变化*小化。相对湿度不应超过标准，硬度过高易加剧数据的可变性。*终，需要控制测试挤压或涂层（印刷）的时间。

达因笔热卖链接：英国舒曼达因笔   

以下为美国ACCU英文参数（附表）：

Recommended Treatment Levels

推荐的表面张力标准

The following chart offers general guidelines regarding the 

required surface treatment levels (as measured by the dyne test)

 for various process/material combinations.Please note it is 

critical that the appropriate specification is determined for 

each job, based on actual empirical results from functional finished 

product testing. The ranges shown here can be used to expedite surface 

analysis by suggesting a reasonable range within which to test. Blind 

reliance on this data will probably reduce your quality costs short t

erm and ensure a large discrepant goods writeoff at some uncertain future date.

以下的表格为在不同的印刷过程和材料的基础上基底材料所需的表面达因值的提供了通用的指引，以下表格的数据是根据实际的测试情况得出的经验数据，表格中所示的合理范围数据可以加快您的表面分析的速度，短期内减少您的质量控制成本。

In most cases, jobs can be run if the substrate – at run-time – is somewhere between the low and high dyne levels cited. For demanding runs (e.g., 

high web speedsand/or critical quality process work), it is safest to shoot for 

the top of the range. Use this chart as a general guideline only: each operation 

has slightly different requirements.These data are for flame&nbs******bsp;

corona treatment in an oxygen-containing atmosphere.

在很多情况下，在测试的时候，被测的基地材料表面不同的地方的达因值在表格所示的*高和*低之间，作为解决办法，应该采用高的那个值。所有测

试数据都是在大气中有氧气的情况下测得的.

NOTES:

(1) Some values theoretical. 一些理论值

(2) Any density, any type, including films, coated board, and molded products. 任何密度，类型，包括薄膜，有图层的板，模塑产品

(3) All types; cast&nbs******bsp;molded. 任何类型，模塑产品

(4) More plasticizer generally requires levels at the high end of these ranges. 比较多的塑化剂需要取范围的上限

(5) Uncoated. 未经涂布的

(6) For heat sealing, the surface energies of the mating PE surfaces should match

 closely; if both faces are treated, heat sealing can usually be accomplished over a

broader and lower temperature range.

对于热封烫合薄膜，和pe 表面的张力必须比较接近，如果是双面处理，热封工艺通常在比较低的温度范围和比较大的面积范围
美国ACCU 达因笔能准确的测试出塑料薄膜之表面张力是否达到试笔的数值。令使用者清楚的了解此薄膜是否适合于印刷，复合或真空镀铝。有效的控制质量及减少因材质不合格所造成的工具延误。它并不**于塑料薄膜，还可以测试各种材料的表面张力。